CS-55 Water Based Acrylic Coating
Surface Preparation Coating and Installation Aid for Concrete and Metal Surfaces. For use on most concrete structures.
SEALING PROPERTIES
- Fast drying concrete damp-proof coating.
- Can be applied effectively with a brush, paint roller or sprayer.
- Soap and water clean up.
- Environmentally responsible. VOC content as low as 59 g/L.
- Suitable for indoor application without specialized paint areas.
- Nearly three times the coverage of typical tar or asphalt based products (300 – 350 sq. ft. per gallon).
- Smooth, hard, polymer film that protects against water intrusion.
- Wide range of standard colors.
- Custom colors available upon request.
- Recycled Content, % by weight:
- Post Industrial: 17%
SPECIFICATIONS
ConSeal CS-55 complies with E.P.A. regulation 40CFR261.4 for solid waste management. CS-55 is made with environmentally safe ingredients; disposal of containers does not present environmental problems.
IMMERSION TESTING
One Year Immersion Testing: No visible deterioration when tested in 5% Caustic Potash, 5% Hydrochloric Acid, 5% Sulfuric Acid, and 5% Hydrogen Sulfide.
PHYSICAL PROPERTIES
| DESCRIPTION | CS-55 |
|---|---|
| COLOR: | Black |
| VISCOSITY: | 2000 – 4000 centapoise |
| MIX INSTRUCTIONS: | Mix lightly prior to use to assure homogenous mix |
| CURE TIME: | Dry to touch in 30-60 minutes at 77°F/50% RH. Subsequent coating application may begin once the previously applied coating is dry to the touch. Complete curing is typically complete in 7 days |
| RECOMMENDED FILM THICKNESS: | 2.0 – 5.0 mils dry (5 – 11 mils wet) |
| COVERAGE RATE: | 344 ft2/gal yields 2 mil dry coverage 229 ft2/gal yields 3 mil dry coverage 172 ft2/gal yields 4 mil dry coverage 138 ft2/gal yields 5 mil dry coverage |
Porosity and concrete surface profile will influence coverage rates.
HEAVY METALS TESTING
| PARAMETER | EPA Limit | CS-55 |
|---|---|---|
| ARSENIC: | 5ppm | BDL |
| BARIUM: | 100ppm | 1.12ppm |
| CADMIUM: | 1ppm | BDL |
| CHROMIUM: | 5ppm | BDL |
| LEAD: | 5ppm | BDL |
| MERCURY: | 0.2ppm | BDL |
| SELENIUM: | 1ppm | BDL |
| SILVER: | 5ppm | BDL |
SCRAPE ADHESION PERFORMANCE
| FILM MILLAGE FORCE | ASPHALT COATING 0.071″ RESULT | CS-55 0.0038″ RESULT |
|---|---|---|
| 500g: | Passed with minimal damage | Passed with no damage |
| 1000g: | Failed 2/3rds of coating scraped off | Passed with no damage |
| 1500g: | Failed, complete film removal | Passed with minimal damage |
| 2000g: | Failed, complete film removal | Passed with minimal damage |
| 2500g: | Failed, complete film removal | Passed with minimal damage |