CS-102 Butyl Rubber Sealant

For concrete joints in: Manholes, Concrete Pipe, Vaults, Box Culverts, Septic Tanks, and Vertical Panel Structures. Not intended for use in expansion joints or joints that move.

SEALING PROPERTIES

  • Provides permanently flexible watertight joints.
  • Low to high temperature workability: 30°F to 120°F (-1°C to +49°C)
  • Rugged service temperature: -30°F to +200°F (-34°C to +93°C)
  • Excellent chemical and mechanical adhesion to clean dry surfaces.
  • Greater cohesive and adhesive strengths.
  • Sealed joints will not shrink, harden or oxidize upon aging.
  • Controlled flow resistance for application ease.
  • No priming normally necessary. When confronted with difficult installation conditions, such as wet concrete or temperatures below 40°F (4°C), priming the concrete will improve the bonding action. Consult Concrete Sealants for the proper primer to meet your application.

HYDROSTATIC STRENGTH

ConSeal CS-102 meets the hydrostatic performance requirement as set forth in ASTM C-990 section 10.1 (Performance requirement: 10psi for 10 minutes in straight alignment – in plant, quality control test for joint materials.)

SPECIFICATIONS

ConSeal CS-102 meets or exceeds all of the requirements of Federal Specification SS-S-210 (210-A), AASHTO M-198 Type B, and ASTM C-990-91.

CHEMICAL COMPOSITION

DESCRIPTION SPEC REQUIRED CS-102
HYDROCARBON PLASTIC CONTENT % BY WEIGHT: ASTM D4 (mod.) 50% min. 51%
INERT MINERAL FILLER % BY WEIGHT: AADHTO T111 30% min. 35%
VOLATILE MATTER % BY WEIGHT: ASTM D6 3% max. 1.2%

IMMERSION TESTING

30-Day Immersion Testing: No visible deterioration when tested in 5% Caustic Potash, 5% Hydrochloric Acid, 5% Sulfuric Acid, and 5% saturated Hydrogen Sulfide.

One Year Immersion Testing: No visible deterioration when tested in 5% Formaldehyde, 5% Formic Acid, 5% Sulfuric Acid, 5% Hydrochloric Acid, 5% Sodium Hydroxide, 5% Hydrogen Sulfide, and 5% Potassium Hydroxide.

DESCRIPTION SPEC REQUIRED CS-102
COLOR: Black
SPECIFIC GRAVITY, 77°F: ASTM D71 1.15 – 1.50 1.25
DUCTILITY, 77°F: ASTM D113 5.0 min. 6 cm
SOFTENING POINT, RING AND BALL °F: ASTM D36 50 – 100 min. 350°F (177°C)
PENETRATION, CONE 77°F: ASTM D217 55-100  dmm. 55-60 dmm
FLASH POINT, C.O.C., °F: ASTM D92 350°F min. 375°F
FIRE POINT, C.O.C., °F: ASTM D92 375°F min. 475°F (232°C) minimum